VIRGIN LLDPE / HDPE / LDPE GRANULES

Application:

LDPE is used in products and packaging such as plastic bags, milk jugs, detergent bottles, margarine tubs, garbage containers, water pipes, woven bag, raincoat, polyethylene monofilament, woven yarn etc.. LDPE resins are made by high pressure autoclave process and mainly used for blown film extrusion and wire coating (cable sheath) etc.. They are widely used for applications for general purpose packaging films, heavy duty bags, shrink films, and foams.

Category:

Description

Film Grade

Item Test condition Test Method Value Unit
Density   ISO 1183 0.944-0.955 g/cm3
MFR 190°C/2.16kg ISO 1133 0.03-0.07 g/10min
Tensile strength at yield   ISO 527-2 22 MPa
Elongation at break   ISO 527-2 >350 %
ESCR F50,50°C,100% ASTM D-1693A 1000 h
VICAT   ASTM D-1525 126 °C

Blow Molding Grade

Item Test Condition Test Method Value Unit
Density   ISO 1183 0.950~0.955 g/cm
MFR 190°C/2.16kg ISO 1133 1.7~2.5 g/10min
Tensile strength at yield   ISO 527-2 24 MPa
Elongation at break   ISO 527-2 >600 %

Injection Grade

Item Test Condition Test Method Value Unit
MFR 190°C/2.16kg ASTM D-1238 20 g/10min
Density ASTM D-792 0.954 g/cm3
Tensile strength at yiled ASTM D-638 28 MPa
Elongation at break ASTM D-638 250 %
Impact tensile strength ASTM D-1822 42 kJ/m2
ESCR   ASTM D-1693 3
VACIT ASTM D-1525 127 °C